Welcome to the world’s most advanced solar backsheet product directory. Panel manufacturers can use our advanced technical filters to find the exact solar backsheet that matches their needs. We have collated backsheet data from manufacturers from all around the world into a common template, allowing you to compare and review backsheets easily.
Layers: | PVF / PET | Tensile Strength: | 120 MPa |
Total Thickness: | 286±14.3 µm | Thermal Shrinkage: ≤ | 1 % |
Region: | China |
Layers: | Coating / PET / Coating | Tensile Strength: | 120 MPa |
Total Thickness: | 318±15.9 µm | Thermal Shrinkage: ≤ | 1 % |
Region: | China |
Double-sided clear coating , reinforced PET structureand printed special mesh
Photovoltaic Back Sheetmaterials Which protect the cells
Layers: | PET | Tensile Strength: | 160 MPa |
Total Thickness: | 280 µm | Thermal Shrinkage: ≤ | 0.6 % |
Region: | China |
Layers: | PET / PET / Primer | Tensile Strength: | 100 MPa |
Total Thickness: | 360±5 µm | Thermal Shrinkage: ≤ | 1.5 % |
Region: | India |
Layers: | PET | Tensile Strength: | 120 MPa |
Total Thickness: | 406±20.3 µm | Thermal Shrinkage: ≤ | 0.6 % |
Region: | China |
Pv backsheets are made by composite of eva adhesive layer made of BR film
Support layer made of weather resistant pet and intermediate layer made of water vapor barrier film
Layers: | Coating / PET / Coating | Tensile Strength: | 130 MPa |
Total Thickness: | 303±15.15 µm | Thermal Shrinkage: ≤ | 0.6 % |
Region: | China |
With double-sided transparent coating andreinforced PET structure
lt is characterized by goodinsulating properties, strong bonding fastness, excellentbarrier and heat and humidity resistance
Layers: | Coating / PET / Coating | Tensile Strength: | 160 MPa |
Total Thickness: | 253±12.65 µm | Thermal Shrinkage: ≤ | 1 % |
Region: | China |
Layers: | PVDF / PET | Tensile Strength: | 140 MPa |
Total Thickness: | 340 µm | Thermal Shrinkage: ≤ | 1.2 % |
Region: | China |
Layers: | Tedlar(PVF) / PET / Tedlar(PVF) | Tensile Strength: | 149 MPa |
Total Thickness: | 323±32.3 µm | Thermal Shrinkage: ≤ | 1.5 % |
Region: | United States |
Layers: | Coating / Polyolefin | Tensile Strength: | 25 MPa |
Total Thickness: | 176 µm | Thermal Shrinkage: ≤ | 1.2 % |
Region: | Germany |